pangang titanium r-248 sulphate process rutile tio2 pigment for masterbatches

pangang titanium r-248 sulphate process rutile tio2 pigment for masterbatches

pangang titanium r-248 Sulfate process rutile tio2 pigment for masterbatches is a general grade of rutile TiO2 pigment. It is produced by sulfate process with high quality ilmenite concentrate from the Panxi area. Advanced inorganic coating by aluminum and zirconium, compound organic treatment has been adopted in production. It has stable performance in application of plastic, presenting bluish undertone, good fluidity, low oil absorption and good application property etc.

Description

pangang titanium r-248 Sulfate process rutile tio2 pigment for masterbatches is a general grade of rutile TiO2 pigment. It is produced by sulfate process with high-quality ilmenite concentrate from the Panxi area. Advanced inorganic coating by aluminum and zirconium, compound organic treatment has been adopted in production. It has stable performance in the application of plastic, presenting a bluish undertone, good fluidity, low oil absorption, and good application property, etc.

Recommended applications

  1. Masterbatch
  2. Multilayer co-extruded film
  3. Plastic pipe
  4. Powder paint

Storage

Avoid damp and sun exposure.

Packing

In 25kg, 500kg, 1000kg

Contact Us


    Additional information

    Weight 24000 kg
    TiO2 Content, %, Min

    96.5

    Rutile Content, %, Min

    97

    Brightness %

    94.9

    L*Value

    97.3

    B*Value

    2.9

    Tint-reducing power

    1870

    Dispersibility Hegman scale (min)

    6.5

    Oil absorption [g/100g] (max)

    15

    Slurry pH

    6.0~9.0

    Specific resistance (min)

    120??.m

    Volatiles 150?? (max)

    0.2

    Sieve residual [%] (45??m)

    0.01

    Inorganic treatment

    Al2O3, ZrO2